Aluminum-iodoform composite reactive material
Ani Abraham
, Shasha Zhang
, Yasmine Aly
,
Mirko Schoenitz
,
Edward L. Dreizin
Chemical and Materials Engineering
Research output
:
Contribution to journal
›
Article
›
peer-review
18
Link opens in a new tab
Scopus citations
Overview
Fingerprint
Fingerprint
Dive into the research topics of 'Aluminum-iodoform composite reactive material'. Together they form a unique fingerprint.
Sort by
Weight
Alphabetically
Keyphrases
Reactive Materials
100%
Iodoform
100%
Room Temperature
66%
Iodine
66%
Ignition Temperature
66%
Particle Size
33%
X-ray
33%
Metal Filament
33%
Cryomilling
33%
Material Characterization
33%
Aerosolized
33%
Diffraction
33%
Thermogravimetric Analysis
33%
Electron Microscopy
33%
Liquid Nitrogen Temperature
33%
Pressure Rise Rate
33%
Maximum Pressure
33%
Constant Volume
33%
Pure Aluminum
33%
Combustion Characteristics
33%
Aluminum Powder
33%
Iodine Concentration
33%
Ball Milling
33%
Thermogravimetric Measurements
33%
Maximum Rate
33%
Al Matrix
33%
Cryogenic Milling
33%
Engineering
Reactive Material
100%
Tincture of Iodine
100%
Aluminum
100%
Iodine
100%
Room Temperature
66%
Prepared Material
66%
Ignition Temperature
66%
Ball Milling
33%
Pressure Rise
33%
Pure Aluminum
33%
Constant Volume
33%
Aluminum Powder
33%
Step Oxidation
33%
Al Matrix
33%
X Ray Diffraction
33%
Nitrogen
33%
Chemistry
Aluminum
100%
Iodine
100%
Iodoform
100%
Ambient Reaction Temperature
66%
X-Ray Diffraction
33%
Thermogravimetric Analysis
33%
Gravimetric Analysis
33%
Filament
33%
Electron Microscopy
33%
Ball Milling
33%
Nitrogen
33%
explosion
33%
Material Science
Aluminum
100%
X-Ray Diffraction
33%
Electron Microscopy
33%
Thermogravimetric Analysis
33%