Abstract
Herringbone carbon nanofibers (CNFs) were efficiently produced by chemical vapor deposition on Ni nanoparticles derived from layered double hydroxide (LDH) precursors. The as-obtained CNFs with a diameter ranging from 40 to 60 nm demonstrated herringbone morphologies when they grew on Ni/Al LDH derived catalysts both in the fixed-bed and fluidized-bed reactor. The Ni/Mg/Al, Ni/Cu/Al, as well as Ni/Mo/Mg/Al catalysts were also effective to grow herringbone CNFs. The diameter and specific surface area of the as-obtained CNFs highly depended on the catalyst composition and the growth temperature. When CNFs were grown at 550 C on Ni/Al catalyst, the as-obtained products had an outer diameter of ca. 50 nm and a specific surface area of 242 m2 g-1, possessed a discharge capacity of 330 mAh g-1 as the electrode in a two-electrode coin-type cell. With the increase of the surface area, the discharge capacity increased at a rate of 0.90 mAh cm-2, while the initial coulombic efficiency decreased gradually on nanocarbon anodes. This is attributed to the fact that CNFs with higher surface area afford smaller sp2 carbon layer that facilitated more Li ions to extract from the anodes.
Original language | English (US) |
---|---|
Pages (from-to) | 393-404 |
Number of pages | 12 |
Journal | Carbon |
Volume | 62 |
DOIs | |
State | Published - Oct 2013 |
Externally published | Yes |
All Science Journal Classification (ASJC) codes
- General Chemistry
- General Materials Science