TY - JOUR
T1 - Understanding Acoustic Cavitation Initiation by Porous Nanoparticles
T2 - Toward Nanoscale Agents for Ultrasound Imaging and Therapy
AU - Yildirim, Adem
AU - Chattaraj, Rajarshi
AU - Blum, Nicholas T.
AU - Goodwin, Andrew P.
N1 - Publisher Copyright:
© 2016 American Chemical Society.
PY - 2016/8/23
Y1 - 2016/8/23
N2 - Ultrasound is widely applied in medical diagnosis and therapy due to its safety, high penetration depth, and low cost. In order to improve the contrast of sonographs and efficiency of the ultrasound therapy, echogenic gas bodies or droplets (with diameters from 200 nm to 10 μm) are often used, which are not very stable in the bloodstream and unable to penetrate into target tissues. Recently, it was demonstrated that nanobubbles stabilized by nanoparticles can nucleate ultrasound responsive microbubbles under reduced acoustic pressures, which is very promising for the development of nanoscale (<100 nm) ultrasound agents. However, there is still very little understanding about the effects of nanoparticle properties on the stabilization of nanobubbles and nucleation of acoustic cavitation by these nanobubbles. Here, a series of mesoporous silica nanoparticles with sizes around 100 nm but with different morphologies were synthesized to understand the effects of nanoparticle porosity, surface roughness, hydrophobicity, and hydrophilic surface modification on acoustic cavitation inception by porous nanoparticles. The chemical analyses of the nanoparticles showed that, while the nanoparticles were prepared using the same silica precursor (TEOS) and surfactant (CTAB), they revealed varying amounts of carbon impurities, hydroxyl content, and degrees of silica cross-linking. Carbon impurities or hydrophobic modification with methyl groups is found to be essential for nanobubble stabilization by mesoporous silica nanoparticles. The acoustic cavitation experiments in the presence of ethanol and/or bovine serum albumin (BSA) demonstrated that acoustic cavitation is predominantly nucleated by the nanobubbles stabilized at the nanoparticle surface not inside the mesopores. Finally, acoustic cavitation experiments with rough and smooth nanoparticles were suggested: a rough nanoparticle surface is needed to largely preserve surface nanobubbles after coating the surface with hydrophilic macromolecules, which is required for in vivo applications of nanoparticles.
AB - Ultrasound is widely applied in medical diagnosis and therapy due to its safety, high penetration depth, and low cost. In order to improve the contrast of sonographs and efficiency of the ultrasound therapy, echogenic gas bodies or droplets (with diameters from 200 nm to 10 μm) are often used, which are not very stable in the bloodstream and unable to penetrate into target tissues. Recently, it was demonstrated that nanobubbles stabilized by nanoparticles can nucleate ultrasound responsive microbubbles under reduced acoustic pressures, which is very promising for the development of nanoscale (<100 nm) ultrasound agents. However, there is still very little understanding about the effects of nanoparticle properties on the stabilization of nanobubbles and nucleation of acoustic cavitation by these nanobubbles. Here, a series of mesoporous silica nanoparticles with sizes around 100 nm but with different morphologies were synthesized to understand the effects of nanoparticle porosity, surface roughness, hydrophobicity, and hydrophilic surface modification on acoustic cavitation inception by porous nanoparticles. The chemical analyses of the nanoparticles showed that, while the nanoparticles were prepared using the same silica precursor (TEOS) and surfactant (CTAB), they revealed varying amounts of carbon impurities, hydroxyl content, and degrees of silica cross-linking. Carbon impurities or hydrophobic modification with methyl groups is found to be essential for nanobubble stabilization by mesoporous silica nanoparticles. The acoustic cavitation experiments in the presence of ethanol and/or bovine serum albumin (BSA) demonstrated that acoustic cavitation is predominantly nucleated by the nanobubbles stabilized at the nanoparticle surface not inside the mesopores. Finally, acoustic cavitation experiments with rough and smooth nanoparticles were suggested: a rough nanoparticle surface is needed to largely preserve surface nanobubbles after coating the surface with hydrophilic macromolecules, which is required for in vivo applications of nanoparticles.
UR - http://www.scopus.com/inward/record.url?scp=84983546632&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84983546632&partnerID=8YFLogxK
U2 - 10.1021/acs.chemmater.6b02634
DO - 10.1021/acs.chemmater.6b02634
M3 - Article
AN - SCOPUS:84983546632
SN - 0897-4756
VL - 28
SP - 5962
EP - 5972
JO - Chemistry of Materials
JF - Chemistry of Materials
IS - 16
ER -